weldmetadvisory

Inquirer:-  For welding a furnace with material P 355GH, we need to select welding consumables. The plate thickness is 22 mm. P355GH Yield strength value is 345 MPa min, Tensile strength 510-650 MPa & it undergoes a process of corrugation forming at 880-910° C and PWHT at 610°C. PROCESS: FCAW +SAW So please suggest consumables for this. …

Filler Metals for P355GH Material meeting PWHT requirements? Read More »

Inquirer:- We did welding LCS to SS 316L by using SS 309L. Weld Metal We checked with PMI Machine, We found it to be of SS 308 compositions. How it is possible? , Kindly clarify it. The process used was GTAW. The chemical composition of the AISI 1018 Steel, ASTM A 240 Type 316L Stainless …

Undesirable Weld Metal Composition of the welded joint between CS and SS 316L using ER309L? What went wrong? Read More »

INQUIRER:- Dear Sir, we have difficulty in meeting 40J CVN value in WM & HAZ at 0 degrees C. It is possible to achieve 40 J CVN value at 0 deg C test temperature in X50 micro-alloy steel with HF-ERW process? in our process, Flat surface is going through roller and joint is made by …

Meeting CVN Impact strength of 40 J at 0 degrees Celcius fabricated with HF-ERW process API X50 grade material pipe Read More »

Dear Sir, Generally, for joining CS/LAS to 300 type Stainless Steel, austenitic filler materials like E/ER 308, 309,316 and 347 are used but these filler metals are used when service application is below 425°C. For higher temperature service application as you mentioned, I would suggest you for using High-Nickel filler metals ERNiCrFe-2, and ENiCrFe-2, ENiCrFe-3. …

Which is Suitable filler metal for joining SS Type 310 and Creep resisting 2.25Cr-1Mo steel for high temperature furnace application ? Read More »